Osteogenic potential of simvastatin loaded gelatin-nanofibrillar cellulose-β tricalcium phosphate hydrogel scaffold in critical-sized rat calvarial defect

Abstract

A new hydrogel scaffold, containing both osteoconductive and osteoinductive properties, was developed for enhanced bone regeneration. Simvastatin loaded Gelatin-nanofibrillar cellulose-β tricalcium phosphate (GNTS) hydrogel scaffold was prepared by the freeze-drying method. Gelatin and β tricalcium phosphate were added to the scaffold to provide osteoconductivity. As an osteoinductive molecule, simvastatin was entrapped in the scaffold. Nanofibrillar cellulose contributed to the slower degradation rate of the scaffold, which in turn favored the sustainable release of simvastatin. Three different concentrations of simvastatin (S) (0.25, 0.5 and 1μM), were loaded in these scaffolds to make GNTS.25, GNTS.5 and GNTS1 scaffolds, respectively. Simvastatin was released from the scaffolds gradually and constantly for up to 30days, with an initial burst release. Cell proliferation on the scaffolds was not perturbed up to 0.5μM simvastatin. Quantitative analysis (PT-PCR) showed that alkaline phosphatase (ALP), osteopontin (OPN) and osteocalcin (OCN) mRNAs, responsible for the osteoblastic differentiation of rat bone marrow mesenchymal stem cells (RBMSCs), were expressed in higher amounts in GNTS.5 scaffold than in other scaffolds. Scaffolds were implanted in critical-sized rat calvarial defects for 4 and 8weeks. Micro-CT and histological analysis revealed that greater extent of bone formation, with higher amount of collagen matrix deposition, was observed in GNTS.5 scaffold at both time points. These results suggest that GNTS.5 scaffold, along with its osteoconductive architecture, releases the optimum concentration of simvastatin to enhance osteogenesis.