In order to clarify the effect of the hydrogen environment on the slip behavior of a low carbon steel JIS S10C, fully reversed bending tests were carried out in hydrogen environment and in nitrogen environment. The main obtained result is as follows. The slip band continued developing over the 10^7 cycles in hydrogen environment. More crystal grains had slipped in hydrogen environment than in nitrogen environment after the fatigue test. This shows that the hydrogen environment prevented slip development from stopping. In order to compare the slip of each crystal grains microscopically in hydrogen environment with nitrogen environment, each crystal orientation is identified through EBSD analysis. The active slip system and Schmid factor of that identified through EBSD analysis and SEM image is also used to observe the slip.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: The Proceedings of the Materials and Mechanics Conference
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.