Abstract
The Stress Corrosion Cracking has been observed in a component of low carbon austenitic stainless steel in the BWRs. It is necessary to examine various factors on the SCC crack propagation for the operation and maintenance and the reliability securing of the aged plant. In this study, the effect of the cyclic load that causes it for SCC crack propagation in simulated BWR environment is examined by using the CT specimen of cold-rolled stainless steels (SUS316L). As a result of the examination, the retardation phenomenon was observed as for the SCC crack immediately after the cyclic load was received.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: The Proceedings of the Materials and Mechanics Conference
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.