Abstract
Hysteresis loops of the nanoscale magnetic layer Co90Fe10 and Ni81Fe19 and bilayer Co90Fe10/Ni81Fe19 and Ni81Fe19/Co90Fe10 films were measured as a function of external dc magnetic field and the thickness dependence of these films were plotted as a function of temperature. Time evolution of the minor/middle/major hysteresis loops of 5/5nm-thick Ni81Fe19/Co90Fe10 monolayer have been observed at 10K. The spin valve, exchange bias training and Barkhausen effects for magnetic layer and bilayer films have been analysed at various temperatures, thicknesses and different orientations according to the substrate. The exchange-bias training effects have been observed only in positive magnetization region. Origin of the exchange-bias training effects and asymmetric hysteresis loops are related to the relaxation mechanism of a pinning layer in magnetically coupled soft/hard bilayers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.