Abstract
AbstractThe lamellar structures in uniaxially drawn films of miscible crystalline/crystalline polymer blends of poly(vinylidene fluoride) (PVDF) and poly(3‐hydroxybutyrate) (PHB) were investigated by static and time‐resolved measurements of small‐angle X‐ray scattering (SAXS). Intense SAXS in the low angle range of the meridian was interpreted as originating from the interlamellar inclusion structure, in which the PHB chains were included between the lamellae of PVDF. The interlamellar inclusion was induced for the uniaxially drawn films of PVDF/PHB = 30/70 blend with a draw ratio (DR) of 2.8–4.5, whereas the lamellae of the PVDF and PHB components were mutually excluded from each other forming their own lamellar stacks (interlamellar exclusion) in the blend with a higher DR (5.0–5.7). When the highly drawn film with the interlamellar exclusion structure was heat treated at 154–165 °C, the interlamellar inclusion structure was partially induced by the heat treatment. The time‐resolved SAXS measurements indicated that the interlamellar inclusion structure was developed by melting and recrystallization of PVDF during the heat treatment. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 381–392, 2009
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Polymer Science Part B: Polymer Physics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.