Abstract
The twinning induced plasticity steel 0.6 C–18 Mn–1.5 Al (wt.%) employed in this study exhibited a strength of about 1GPa, combined with a large uniform elongation of over 60% at moderate strain rates. This excellent combination of tensile mechanical properties was shown to be a result of complex dynamic strain-induced microstructural reactions, including dislocation glide, dislocation dissociation, stacking fault formation, dynamic recovery, mechanical twinning and dynamic strain ageing. The contribution of each of these processes was discussed with respect to the strain hardening behaviour. An important observation was that the propensity for mechanical twinning in a particular grain strongly depends on its crystallographic orientation and is clearly correlated with the magnitude of the corresponding Taylor factor. The current results reveal that the development of partial dislocations and stacking faults at an early stage of straining and the consequent interaction of gliding dislocations with stacking fault interfaces enhances the strain hardening rate. Subsequent or concurrent initiation of mechanical twins also contributes to strain hardening through a dynamic Hall–Petch effect limiting the dislocation mean free path and consequently enhancing dislocation storage. Dynamic strain ageing (DSA) took place at a late stage of deformation, adding to strain hardening. DSA is a factor reducing ductility by promoting strain localization.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.