Abstract
AbstractSummary: A study of the structure–property relationships for nanocomposites prepared by melt compounding from ethylene–acrylic acid copolymers of varied composition and molecular architecture, and organoclays modified with different ammonium ions has been made by DSC, POM, SEM, TEM, WAXD, and rheological and mechanical tests. Within the series of clays investigated, the best levels of dispersion were displayed by those organically modified with quaternary ammonium ions containing two long alkyl tails. The relevant nanocomposites were shown to possess mixed exfoliated and intercalated morphology. The spacing of the intercalated clay stacks, most of which comprise few silicate layers, was found to be independent of clay loading, in the range of 2–50 phr, and to change with the molecular architecture of the matrix polymer. An indication that the excess surfactant present in some of the clays, and the organic material added in others to expand the interlayer spacing, were expelled from the clay galleries during melt blending and acted as plasticisers for the matrix polymer, was obtained from WAXD and rheological characterisations.TEM micrograph of the nanocomposite of EAA1 with 11 phr of 15A.magnified imageTEM micrograph of the nanocomposite of EAA1 with 11 phr of 15A.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.