Abstract
Stearyltrimethyl ammonium bromide(STAB) was used for organic modification of bentonite and then ball milled the modified bentonite. The organically modified bentonite was analyzed by FT-IR and XRD. The results show that the stearyltrimethyl ammonium bromide has been interalated into the layers of bentonite. The layer distance of the bentonite is increased from 1.256nm to 2.694nm. The appropriate experimental conditions of interplanar spacing increasing were the dosage of STAB 40%, reaction time 4h, temperature 75°C. The ball milled organically modified bentonite was analyzed by SEM. The results show that the particle mainly reach submicron to nanometer when ball mill 2h. The particle size distribution range is from 100nm to 500nm. Ball milled organically modified bentonite/ cationic guar gum(CGG) can improve retention rate of paper-process reconstituted tobacco pulp obviously than organically modified bentonite/CGG because of smaller grains and better unigormity of ball milled bentonite.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.