The microstructure of lead-free 0.94(Na0.5Bi0.5)TiO3–0.06BaTiO3 (BNBT-6) piezoelectric ceramics was investigated by different analysis techniques. X-ray diffraction (XRD) result reveals the coexistence of rhombohedral and tetragonal symmetry in the structure of BNBT-6 ceramics at room temperature. Selected area electron diffraction (SAED) patterns reveal the presence of ordered domains in BNBT-6 ceramics. The superlattice reflections {h+1/2 k+1/2 0} and {h+1/2 k+1/2 l+1/2} of ordered domains mainly come from the octahedral tilt and chemical ordering of A-site atoms. High-resolution transmission electron microscopy (HRTEM) combined with image processing is an effective method to investigate the defects and the size of ordered domains in BNBT-6 ceramics. One-dimensional fringe images of superlattice reflections indicate that there are significant local Na and Bi atomic layer displacements and anti-phase boundaries as a result of chemical ordering, which provide a driving force for order–disorder transformation. A filtered HRTEM black/white image shows the size of ordered domains to be about 5–10nm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.