Abstract
In this study, hard coatings (TiN, TiCN, CrN, and CrCN) and Me-DLC coatings (Tix%-C:H and Crx%-C:H) were deposited on tungsten carbide (WC) substrate by multiarc physical vapor deposition (MAPVD) and unbalanced magnetron (UBM) sputtering, respectively. Counterbodies of the AISI 1045 steel cylinder and the AA7075T651 aluminum cylinder were used in the cylinder-on-disk, line-contact wear mode under dry condition; a counterbody of the AISI 52100 steel ball was used in the ball-on-disk, point-contact wear mode, under both dry and lubricated conditions. All wear tests were conducted with a reciprocating machine. After the tests, the most suitable coating for various counterbodies and test environments was selected. For the coating/1045 steel cylinder, the Ti10%-C:H coating possesses excellent tribological characteristics. For the coating/7075T651 aluminum cylinder, hard coatings display excellent wear resistance. For the coating/steel ball, CrCN and CrN coatings display very little wear under both dry and lubricated conditions. On TiN and TiCN coatings, special wear mechanisms of material transfer, adhesion wear, and fatigue fracture occurred during initial tests under kerosene lubrication.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.