Abstract
In order to obtain the good match between yield strength and low-temperature toughness, the short-time partial austenitization (SPA) process was employed for V/Mo-bearing 0.22C-5.24Mn steel. The initial microstructure after intercritical tempering was dual-phase ferrite and reversed austenite (RA), while the final microstructure consisted of ferrite, RA, and secondary martensite (SM) after being subjected to the SPA process. (V, Mo)C with disclike morphology mainly precipitated during intercritical tempering, and the aspect ratio of particles decreased, leading to the appearance of near-spherical morphology. After being subjected to SPA process, the resultant multiphase hierarchical microstructure (three layers: outer layer of ferrite, interlayer of SM, and inner layer of RA) enabled a high yield strength of 1097 MPa, a total elongation of 14%, and an impressive impact energy of 33.3 J at -20 °C. The strengthening contribution of (V, Mo)C precipitation was estimated to be about 108 MPa.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.