Abstract
This paper presents the optimal conditions for the design of a single-rod fluxgate magnetometer using Co-based amorphous magnetic wires with reduced geometrical dimensions of 100 μm in diameter. In order to enhance the performance of the current sensor (i.e. the noise level, the sensitivity, the dynamical range, the scaling factor, etc), the core materials were subjected to annealing at different annealing temperatures in a longitudinal magnetic field ranging from 0 to 0.5 T. The B–H measurements have shown that the heat treatments significantly change the magnetic parameters of the cores (the saturation field, the initial and apparent permeabilities). For instance, the initial permeability μi attains values of between 3500 and 4700 depending on the treatment conditions. These magnetic parameters were subsequently correlated with the sensor performance by using the principles of the fluxgate physics. Consequently, the enhanced fluxgate effect with improved sensing characteristics has been obtained by annealing the wire core at 250 °C (B = 0 T). It is shown that this magnetic wire with a sensing area of 0.00785 mm2 is suitable as a sensor core for the nondestructive testing of metallic objects and the surfaces of magnetic cards. The sensor signal shows perfect linear dependence to dc or low frequency fields up to ~1 Oe. The fitting parameters R2 of 0.9998 could be achieved in a dc field interval of −1.0 Oe and 1.0 Oe (when R2 =1.0, all points lie exactly on the curve with no scatter). Such linearity has not been seen in such a large dynamical range until now in the rod-type single-core fluxgates. It is also shown that there is no hysteresis on the V2f–Hdc graphs (the V2f is the sensor signal) even after applying fields as high as 100 Oe. Besides, the cross-field effect is almost zero due to the geometry of the long-thin wire.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.