Abstract
Wide bandgap semiconductors such as ZnSe and ZnO have attracted great interest due to their applications in solar cells, light emitting diodes, and lasers. However, these wide bandgap semiconductors are frequently difficult to be doped to heavy concentrations, greatly limiting their application. A substrate holder with a natural temperature gradient was developed for batch growth of films at different deposition temperatures, in order to investigate ZnSe film growth and doping challenges. Thin ZnSe films were grown by pulsed laser deposition and characterized using X-ray diffraction, optical transmission and reflection, Raman spectroscopy, and Energy Dispersive X-ray analysis. Deposition temperature and film stoichiometry (Zn:Se) are shown to be significant factors affecting ZnSe growth and doping. ZnSe films with improved crystallinity have been obtained by enriching with selenium and depositing at an optimized temperature. Heavily p-type ZnSe films with hole concentrations of ~2.7 × 1019 cm−3 and resistivities of ~0.099 Ohm cm have been obtained (compared with previous reports of ~1 × 1018 cm−3 and ~0.75 Ohm cm). The results, which are consistent with previous theoretical prediction of compensating defects in ZnSe films, can help to optimize ZnSe growth conditions and understand doping challenges in wide bandgap semiconductors.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.