Abstract
The analysis of the mineralogical composition of most rock wastes shows the presence of a high percentage of minerals with SiO 2 and Al 2O 3, which could be used as raw materials for ceramic products. The main objective of this work is to recover wastes from one primary rock industry, utilised in the production of tiles and flooring, for the manufacturing of ceramics, using powder technology: pressing and sintering. The sinterability of the powders, with and without previous heat treatment, was studied in order to obtain a product with the best performance. Powders from different quarries after being uniaxial pressed at 40 MPa, or isostatic pressed at 170 MPa and sintered within the range 1150–1170°C present properties as follows: (a) hardness: 5.5–7.5 GPa; (b) transverse rupture strength: 55–94 MPa; (c) abrasion and erosion wear better than that of bulk to be drawn materials, and (d) water absorption of less than 0.5%. The results allow the conclusion that these wastes can be recovered and used successfully in the manufacture of ceramics with better performance than traditional tiles and flooring.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.