Abstract
To reduce the solidification structure defects and the macrosegregation of the Φ300 mm continuous casting round bloom, the pulsed magneto‐oscillation (PMO) treatment is added at the secondary cooling zone. A numerical model for calculating the pulsed electromagnetic field, flow field, and temperature field in continuous casting is established, and the coupling simulations of multiphysical fields under different casting parameters and PMO parameters are performed. Their influence on solidification process and the appropriate parameters are discussed. The industrial experiments conducted under the recommended parameters yield good results. Industrial experiments show that when the peak current is increased from 1350 to 1550 KIA and the casting speed is increased from 0.75 to 0.90 m min−1, PMO can increase the equiaxed grain zone and reduce the carbon macrosegregation of the bloom. Moreover, at high casting speed, PMO treatment can significantly promote columnar‐to‐equiaxed transition and increase the width of mixed grain zone.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.