Optimization of Process Parameters for 40Cr Steel Continuous Casting Round Bloom with Pulsed Magneto‐Oscillation Treatment

Abstract

To reduce the solidification structure defects and the macrosegregation of the Φ300 mm continuous casting round bloom, the pulsed magneto‐oscillation (PMO) treatment is added at the secondary cooling zone. A numerical model for calculating the pulsed electromagnetic field, flow field, and temperature field in continuous casting is established, and the coupling simulations of multiphysical fields under different casting parameters and PMO parameters are performed. Their influence on solidification process and the appropriate parameters are discussed. The industrial experiments conducted under the recommended parameters yield good results. Industrial experiments show that when the peak current is increased from 1350 to 1550 KIA and the casting speed is increased from 0.75 to 0.90 m min−1, PMO can increase the equiaxed grain zone and reduce the carbon macrosegregation of the bloom. Moreover, at high casting speed, PMO treatment can significantly promote columnar‐to‐equiaxed transition and increase the width of mixed grain zone.