Abstract
High optical quality chirowaveguides have been successfully prepared using a synthesized chiral organo-modified silane (ORMOSIL) precursor chemically transformed to a pre-condensed active material prior to dip coating. The chemical and physical parameters are optimized to elaborate in a single step dip coating 4.5μm thick planar chirowaveguides presenting low loss (<1dB/cm). The refractive index can be adjusted from 1.630 to 1.655 at 543.5nm by adding tetraethoxysilane (TEOS) in the solution and by increasing the annealing temperature and time. It is shown that only 10% racemization occurs when annealing is conducted under vacuum at temperature lower than 120°C during less than 10h. Finally, the highest specific optical rotation (OR) obtained is 7°/mm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.