Abstract
Zirconia ceramic is a significant structural material, but its use under some extreme circumstances is limited by its mechanical properties. In this work, SiC particles (SiCp) were added into alumina toughened zirconia ceramics to prepare ZrO2–Al2O3-SiCp ceramics with high performance by using oscillatory pressure sintering (OPS). Results showed that the best OPS temperature of 1600 °C was obtained, and the optimal SiCp particle size and content were 200 nm and 10 vol% respectively. Under these conditions, the specimen exhibited higher mechanical properties including Vickers hardness of 15.43 GPa, bending strength of 1162 MPa and fracture toughness of 6.36 MPa m1/2. Moreover, it was found that the atomic matching between ZrO2/SiCp, Al2O3/SiCp, and ZrO2/Al2O3 was much higher, showing the coherent interface relationship. Therefore, it was favorable for enhanced mechanical properties of as-prepared ZrO2–Al2O3-SiCp ceramics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.