Optimization of La 0.6Ca 0.4Fe 0.8Ni 0.2O 3–Ce 0.8Sm 0.2O 2 composite cathodes for intermediate-temperature solid oxide fuel cells

Abstract

Sample of nominal composition La 0.6Ca 0.4Fe 0.8Ni 0.2O 3 (LCFN) was prepared by liquid mix method. The structure of the polycrystalline powder was analyzed with X-ray powder diffraction data. This compound shows orthorhombic perovskite structure with a space group Pnma. In order to improve the electrochemical performance, Sm-doped ceria (SDC) powder was added to prepare the LCFN–SDC composite cathodes. Electrochemical characteristics of the composites have been investigated for possible application as cathode material for an intermediate-temperature-operating solid oxide fuel cell (IT-SOFC). The polarization resistance was studied using Sm-doped ceria (SDC). Electrochemical impedance spectroscopy measurements of LCFN–SDC/SDC/LCFN–SDC test cell were carried out. These electrochemical experiments were performed at equilibrium from 850 °C to room temperature, under both zero dc current intensity and air. The best value of area-specific resistance (ASR) was for LCFN cathode doped with 10% of SDC (LCFN–SDC9010), 0.13 Ω cm 2 at 850 °C. The dc four-probe measurement exhibits a total electrical conductivity over 100 S cm −1 at T ≥ 600 °C for LCFN–SDC9010 composite cathode.