Abstract
In this research the influence of dynamic CH 4 heat treatment on Sr -hexaferrite has been investigated. With the gas heat treatment, the phase composition, particles size and the morphology of Sr -hexaferrite change significantly. Due to this, the hard magnetic nature of the material changes from hard to soft. The strontium hexaferrite powder was prepared by conventional route with calcination of the mixture of strontium carbonate and hematite at 1100°C for 1 hour. Then the resultant Sr -hexaferrite was isothermally heat treated in methane dynamic atmosphere at various temperatures and gas flows for different times. The rate of heating and cooling were 10°C/min. The optimum conditions were obtained at 950°C and 15CC/min flow for 0.5 hour. The effects of gas heat treatment on the phase composition and the particles size and morphology were characterized by X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and Vibration Sample Magnetometery (VSM) techniques. The results show the decomposition of Sr -hexaferrite and reduction of the resultant hematite mainly to iron. The crystallite size of the resultant iron was also measured below 50nm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Modern Physics: Conference Series
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.