Optimization of deep penetration laser welding of thick stainless steel with a 10 kW fiber laser

Abstract

Deep penetration laser welding of 12mm thick stainless steel plates was conducted using a 10kW high-power fiber laser. The effect of the processing parameters on the weld bead geometry was examined, and the microstructure and mechanical properties of the optimal joint were investigated. The results show that the focal position is a key parameter in high-power fiber laser welding of thick plates. There is a critical range of welding speed for achieving good full penetration joint. The type of top shielding gas influences the weld depth. The application of a bottom shielding gas improves the stability of the entire welding process and yields good weld appearances at both the top and bottom surfaces. The maximum tensile stress of the joint is 809MPa. The joint fails at the base metal far from the weld seam with a typical cup–cone-shaped fracture surface. The excellent welding appearance and mechanical properties indicate that high-power fiber laser welding of a 304 stainless steel thick plate is feasible.