Optimization of conventional-zeolite-synthesis from waste pumice for water adsorption

Abstract

This research reports conventionally-synthesized-zeolites with comparatively large surface area (SSA) and water-uptake prepared solely from waste-pumice. Notably, the synthesis process avoided using additional commercial raw materials, organic templates, and high temperatures, so that the process was less costly and ecofriendly. To optimize the process, the synthesis time was varied, and the mixture of the raw material and alkaline solution was stirred for 12 h. The zeolite mother liquor was also recycled. Water adsorption experiments were carried out using gravimetric measurements. The Na-P1-rich zeolite product with an optimal water uptake of 0.256 g/g was synthesized after 48 h of hydrothermal activation (H). On the other hand, the product’s optimal SSA of 186 m2/g was achieved after 36H under similar conditions (rich in faujasite). Adsorption isotherms showed that water uptake increased with activation time and with the inclusion of mother liquor recycling. Furthermore, recycling resulted in a product with enhanced SSA compared to its precursor. Un-recycled products exhibited relatively high-water uptake both at low and high relative-pressure, while the recycled product had a high uptake at high relative pressure. All products could be used in adsorption heat pump (AHP) applications (air conditioning) suited for high relative humidity (RH) environments. However, high-synthesis-time non-recycled products could also work for low RH AHP applications.