Optimization of barrier layer thickness in MgSe/CdSe quantum wells for intersubband devices in the near infrared region

Abstract

The authors report the optimization of MgSe barrier thickness in CdSe/MgSe multiple quantum well structures and its effect on structural, optical qualities and intersubband (ISB) transition characteristics. Three samples with the MgSe thicknesses of 2 nm, 3 nm, and 4 nm were grown on InP substrates by molecular beam epitaxy. X-ray diffraction and photoluminescence measurements showed that the thinner the MgSe barrier thickness the better the structural quality. However, ISB absorption was only observed in the sample with a MgSe thickness of 3 nm. Failing to observe ISB absorption in the sample with a thicker MgSe barrier (≥4 nm) is due to the deteriorated material quality while the missing of ISB transition in the sample with thinner barrier (≤2 nm) is due to the tunneling of electrons out of the CdSe wells. The optimized MgSe barrier thickness of around 3 nm is found to be able to suppress the electron tunneling while maintaining a good material quality of the overall structure.