Abstract
A Fe–26Al–5Cr (at.%) single-phase (α:A2/B2/D0 3) alloy and two-phase (α+TiC) alloys with different amounts of TiC particles have been hot rolled at 800 °C and the kinetics of static recrystallisation have been studied. In the alloys with a high amount of TiC, needle-like TiC of more than 1 μm in length formed during cooling after homogenisation in the α single-phase region and coarsened during hot rolling. The large particles cause particle stimulated nucleation (PSN) and hence accelerate recrystallisation. In order to accomplish both strengthening by precipitates and inhibition of recrystallisation that deteriorates room-temperature ductility, a thermo-mechanical treatment consisting of hot deformation with a low amount of precipitates and a subsequent heat treatment for further precipitation is proposed. This process is difficult to carry out in the (Fe–26Al–5Cr)–TiC system due to the high precipitation temperature of TiC. The precipitation temperature is significantly decreased by replacing TiC by VC or MoC.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.