Abstract
Pure and Cu+2 doped TiO2 thin films have been successfully deposited onto glass substrate by sol–gel dip-coating. The films were annealed at 450°C for 1h and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM-EDX), atomic force microscopy (AFM), UV–vis spectrophotometer and photocatalytic degradation of methylene blue. XRD confirmed the presence of two phases at higher Cu concentration; TiO2 anatase and CuO. AFM analysis showed that the surface roughness increases within increasing Cu content as well as the presence of large aggregates at higher Cu content. SEM observations confirmed the granular structure of the films, and EDX analysis revealed a low solubility limit (effective doping) of Cu into TiO2 lattice. It was found that the optical band gap energy decreases with increasing Cu content. At constant irradiation time, the photo-degradation of methylene blue rate decreased with increasing concentration of Cu+2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.