Optical, structural, and chemical properties of CR-39 implanted with 5.2 MeV doubly charged carbon ions

Abstract

Poly-allyl-diglycol-carbonate (CR-39) specimens were irradiated with 5.2 MeV doubly charged carbon ions using Pelletron accelerator. Ion dose was varied from 5 × 1013 to 5 × 1015 ions cm−2. Optical, structural, and chemical properties were investigated by UV–vis spectroscopy, x-ray diffractometer, and FTIR/Raman spectroscopy, respectively. It was found that optical absorption increases with increasing ion dose. Absorption edge shifts from UV region to visible region. The measured opacity values of pristine and ion implanted CR-39 range from 0.0519 to 4.7959 mm−1 following an exponential growth (9141%) with the increase in ion dose. The values of direct and indirect band gap energy decrease exponentially with an increase in ion dose by 59% and 71%, respectively. However, average refractive index in the visible region increases from 1.443 to 2.864 with an increase in ion dose, by 98%. A linear relation between band gap energy and crystallite size was observed. Both the number of carbon atoms in conjugation length and the number of carbon atoms per cluster increase linearly with the increase in ion dose. FTIR spectra showed that on C+2 ions irradiation, the intensity of all bands decreases gradually without appearance of any new band, indicating degradation of polymer after irradiation. Raman spectra revealed that the density of −CH2− group decreases on C+2 ions irradiation. However, the structure of CR-39 is completely destroyed on irradiation with ion dose 1 × 1015 and 5 × 1015 ions cm−2.