Abstract
Optical ceramics based on YSAG : Yb : Er with the compositions {Y1.86Yb0.45Er0.09Sc0.6}[Al1.6Sc0.4]Al3O12 and {Y2.26Yb0.45Er0.09Sc0.2}[Al1.0Sc1.0]Al3O12 were fabricated by vacuum sintering from pre-synthesized nanocrystalline powders. A comparative analysis of these samples with optical ceramics of the compositions {Y2.34Yb0.45Er0.09Sc0.12}[Al1.92Sc0.08]Al3O12 and {Y0.96Yb0.45Er0.09Sc1.50}[Al1.8Sc0.2]Al3O12 was carried out. The influence of scandium cations in the dodecahedral and octahedral positions of the garnet crystal lattice on the refractive index of YSAG : Yb : Er, as well as the values of absorption coefficients, integral luminescent intensities, and lifetimes of excited states of Yb3+ (2F7/2 and 2F5/2) and Er3+ (4I15/2, 4I13/2, 4F9/2, and 4S3/2) cations was revealed in the wavelength ranges 520–700 nm and 890–1690 nm. It has been shown that by changing the concentrations of scandium cations in the dodecahedral and octahedral positions of the crystal lattice of YSAG : Yb : Er solid solutions, it is possible to purposefully change the efficiency of energy transfer from ytterbium cations to erbium cations.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.