Abstract
We report on the optical properties of ZnWO(4) planar waveguides created by ion implantation, and the effect annealing has on these structures. Planar optical waveguides in ZnWO(4) crystals are fabricated by 5.0 MeV carbon ion implantation with a fluence of 1 × 10(15) ions/cm(2) or 500 keV helium ion implantation with the a fluence of 1 × 10(16) ions/cm(2). The thermal stability was investigated by 60 minute annealing cycles at different temperatures ranging from 260°C to 550°C in air. The guided modes were measured by a model 2010 prism coupler at wavelengths of 633 nm and 1539 nm. The reflectivity calculation method (RCM) was applied to simulate the refractive index profile in these waveguides. The near-field light intensity profiles were measured using the end-face coupling method. The absorption spectra show that the implantation processes have almost no influence on the visible band absorption.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.