Abstract
ABSTRACTMolecular beam epitaxy-grown GaN with different Mn concentrations (5–23 × 10 cm-3) and codoped with Si were investigated by cathodoluminescence (CL) spectroscopy and optical transmission measurements. In the GaN:Mn, an intense absorption peak at 1.414 +/- 0.002 eV was observed. This peak was attributed to an internal T2∼> E transition of the deep neutral Mn3+ state since its intensity scaled with the Mn3+ concentration. The CL measurements showed that Mn-doping concentrations around 1020 cm-3 had three effects on the emission spectrum: (i) the donor bound exciton at 3.460 eV was reduced by more than one order of magnitude, (ii) the donor-acceptor-pair band at 3.27 eV was completely quenched and (iii) the yellow luminescence centered at 2.2 eV was the strongly decreased. The latter two effects were attributed to a reduced concentration of VGa. In the infrared spectral range, three broad, Mn-doping related CL emission bands centered at 1.01 ± 0.02 eV, 1.09 ± 0.02 eV and 1.25 ± 0.03 eV were observed. These bands might be related to deep donor complexes, which are generated as a result of the heavy Mn-doping, rather than internal transitions at the Mn atom.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.