Abstract

In this study, a cast synthesis approach was used to create flexible nanocomposite films made of polyacrylamide (PAM), chitosan (Cs), and zinc ferrite nanoparticles (ZnFe2O4 NPs). XRD analysis was used to examine the composite structure. They demonstrated the effective interaction between ZnFe2O4 NPs and PAM/Cs blend. As the concentration of nanomaterial in the host polymer matrix grew, it was observed that the PAM/Cs matrix's direct and indirect energy band gaps decreased while its absorbance of ultraviolet–visible radiations increased. The nanocomposite's AC conductivity was significantly higher than that of the blend, and 2.5 wt percent of the nanocomposite showed the highest electrical conductivity. It was observed that as frequency raised, the ε′ and ε″ declined though the concentration of nanoparticles enhanced these characteristics. Because of the high dielectric permittivity of ZnFe2O4, the values of ε′ and ε″ raised as ZnFe2O4 were higher. The outcome of the vibrating sample magnetometer (VSM) demonstrated the ferromagnetic property of the produced nanocomposites. Furthermore, the VSM study shows that as the nanoparticles content increases, the PAM/Cs/ZnFe2O4 nanocomposites' Ms, Hc, and Mr also increase. These PAM/Cs/ZnFe2O4 films were shown by the experimental results to be promising candidates for bandgap-regulated materials, electromagnetic interference shielders, frequency tunable nanodielectric, and flexible dielectric substrates for future microelectronic, optoelectronic technologies, and capacitive energy storage.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.