Abstract
Porous alumina was fabricated and optically characterized over a wide spectral range. Layers were formed electrochemically in oxalic acid solution from 10-μm-thick aluminum films evaporated onto silicon wafers. The layer formation was monitored with in situ spectroscopic ellipsometry in the visible and near-infrared wavelength range to accurately determine the thickness and dielectric functions. Anisotropy due to the columnar nature of the porous structure was determined using optical modeling. The porous alumina layer was found to have a small but significant absorption tail throughout the visible region. Atomic force microscopy and scanning electron microscopy were used throughout the process to assess the quality of pore formation. The mean pore center-to-center spacing was approximately 100 nm with thicknesses up to 5μm. The infrared spectra revealed absorption peaks previously seen in ceramic alumina and peaks not associated with bulk alumina.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.