We report the growth mechanism and optical characteristics of type-II band-aligned GaSb quantum dots (QDs) grown on GaAs using a droplet epitaxy-driven nanowire formation mechanism with molecular beam epitaxy. Using transmission electron microscopy and scanning electron microscopy images, we confirmed that the QDs, which comprised zinc-blende crystal structures with hexagonal shapes, were successfully grown through the formation of a nanowire from a Ga droplet, with reduced strain between GaAs and GaSb. Photoluminescence (PL) peaks of GaSb capped by a GaAs layer were observed at 1.11 eV, 1.26 eV, and 1.47 eV, assigned to the QDs, a wetting-like layer (WLL), and bulk GaAs, respectively, at the measurement temperature of 14 K and excitation laser power of 30 mW. The integrated PL intensity of the QDs was significantly stronger than that of the WLL, which indicated well-grown GaSb QDs on GaAs and the generation of an interlayer exciton, as shown in the power- and temperature-dependent PL spectra, respectively. In addition, time-resolved PL data showed that the GaSb QD and GaAs layers formed a self-aligned type-II band alignment; the temperature-dependent PL data exhibited a high equivalent internal quantum efficiency of 15 ± 0.2%.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.