Abstract
ZnO and ZnS structures were obtained by the calcination of the aqueous precipitation products of Zn(NO3)2, NaOH and l-cysteine (Cys). Initial Cys:Zn molar ratios were changed as 0.1:1, 0.5:1, 1:1 and 1.5:1. All the precursors were transformed into ZnO upon calcination at 700 °C. ZnS structures were obtained by calcining the precursors prepared at the Cys:Zn ratios of 1 and 1.5 at 350 °C. In addition to changing chemical composition of the precipitation products, calcination temperature and initial Cys:Zn ratio also affected morphology, surface area, photoluminescence and photocatalytic properties of the final products. Free exciton energy values of the ZnO samples were observed to be between 3.29 eV and 3.35 eV. PL spectra of the ZnO samples indicated blue and green emission centers. Zinc interstitials (Zni), revealed by the blue emissions in the PL spectra were also confirmed by Auger Zn L3M4.5M4.5 spectra. The samples calcined at 350 °C removed rhodamine B mainly by adsorption. All the samples calcined at 700 °C successfully degraded the dye under UV light. Among the samples calcined at 700 °C, ZnO sample prepared at Cys:Zn = 0.5, which has the highest surface area and unique photoluminescence spectrum exhibited the fastest photodegradation rate.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.