Core–shell Fe3O4@C magnetic nanoparticles which are of great interest for research have a widely applied prospect. However, people know little about the optical and magnetic properties of the small-size Fe3O4@C nanoparticles due to the difficulty of uniformly coating small size Fe3O4 nanoparticles. In this paper, the influence of carbon shell coating on the optical and magnetic properties of small size Fe3O4 nanoparticles was presented. Carbon coating can strengthen the absorption intensity in the UV–visible light region through the introduction of oxygen defects on the surface of the nanoparticles by nitric acid treatment. Fe3O4 and Fe3O4@C nanoparticles both display typical superparamagnetic behavior in the high-temperature regime and a blocked state at low temperature from hysteresis loop, zero-field cooled and field cooled curves. Carbon coating reduce the surface uniaxial anisotropy, thus the average blocking temperature <TB> decreases from 59 K of Fe3O4 nanoparticles to 50 K of Fe3O4@C nanoparticles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.