Abstract
A series of glass with appropriate chemical compositions (60-x) P2O5 + 20 Bi2O3 + 10 SrF2 + 10 Na2 CO3 + x Nd2O3, (x = 0.1, 0.5, 1.0, 1.5, and 2.0% by mole) were prepared by using the melt quenching technique. The glass phase structure was confirmed by using X-ray diffraction technique. The structural analysis using FTIR technique it reveals characteristic bonding vibrations and different functional group in the glass matrix. The elements present in the fabricated glass sample was analyzed by using EADX spectrum. J-O intensity parameters Ω2, Ω4, and Ω6for the currently being researched PBNSNd10 glass have values of 9.80 × 10-20 cm2, 3.305 × 10-20 cm2, and 5.576 × 10-20 cm2 sequentially. The J-O parameters shows a trend of Ω2 > Ω6 > Ω4. The near infrared emission spectra recorded with 808 nm laser diode excitation for various concentrations of neodymium ions show the emission intensity is highest for the 4F3/2 → 4I11/2 transition at 1056 nm. The measured decay times 4F3/2 level decreased with increasing Nd2O3 ions because of concentration quenching effect. The obtained results in present study have been compared with previous results obtained for Nd2O3 doped glasses.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.