Abstract
Single-wall carbon nanohorn (SWNH), which is a tubular particle with a cone cap, was oxidized in an oxygen flow at various temperatures. N(2) adsorption at 77 K, thermogravimetry (TG), differential thermal analysis (DTA), transmission electron microscopy, and Raman spectroscopy measurements were carried out on the oxidized SWNHs. The specific surface area of the oxidized SWNHs can be controlled by oxidation temperature, giving the maximum value of 1420 m(2)/g. The pore size distribution by the BJH method and the comparison plot of the N(2) adsorption isotherms of SWNH oxidized at different temperatures against that of as-grown SWNH revealed the minimum oxidation temperature for opening internal nanopores. TG-DTA analyses determined the components of as-grown SWNH: amorphous carbon 2.5 wt %, defective carbon at the cone part 15 wt %, tubular carbon 70 wt %, and graphitic carbon 12 wt %. These systematic analyses provided the exact internal nanopore volume of 0.49 mL/g for pure SWNH particles.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.