Abstract

Manganese (Mn) grows in a metastable expanded (c/a > 1) face-centered-tetragonal (fct) phase on thin fct-Co(001) template films. A layer-by-layer growth mode is observed for small Mn thicknesses. Antiferromagnetism (AFM) of fct-Mn is evidenced by the observation of shifted magnetization loops antiparallel to the cooling field direction (negative bias) and enhanced coercive fields for Co/Mn bilayers. At low temperature, magnetic exchange interactions are detected at the Co/Mn interface for nominal Mn thicknesses as low as 1.4 monolayer (ML), indicating the onset of AFM in 2-ML-thick Mn islands. However, between 2- and 5-ML Mn, a positive bias of the magnetization loops is observed in a certain temperature range below the blocking temperature (TB) of the films. This peculiar behavior is explained by the dependence of TB on both the local Mn ML thickness and the Mn island size, leading to a unidirectional coercivity enhancement in a temperature range where both blocked and unblocked regions coexist in the Mn layers.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.