Abstract
An investigation on varying experimental parameters such as solution quantity (2.5, 5 and 7.5 mL) and reaction time (15, 30, 45 and 60 min) was carried out for the production of high-quality multiwalled carbon nanotubes (MWCNTs) in one step pyrolysis. Structural analysis revealed the uniform diameter distribution and the length of nanotubes in the range of 60-80 nm and 0.4-2 μm, respectively. Raman and X-ray diffraction analysis showed a remarkable reduction in defect density with increase in graphitization degree, upon increasing the solution volume and reaction time. MWCNTs prepared at higher solution quantity (7.5 mL) with higher reaction time (60 min) showed higher crystallinity (70% graphitization) and lower defect density (ID/IG: 0.56). The attainment in equilibrium of evaporation cum precipitation in formation of high quality nanotubes structure is evaluated. An effective resupplying of condensed precursors by re-evaporation leads for the achievement of low defect density nanotubes with higher product yield is achieved.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.