Abstract
A facile one-step solution-phase chemical reduction method has been developed to synthesize Ag microsheets at room temperature. The morphology of Ag sheets is a regular hexagon more than 1 μm in size and about 200 nm in thickness. The hexagonal Ag microsheets possess a smoother and straighter surface compared with that of the commercial Ag micrometer-sized flakes prepared by ball milling for electrically conductive adhesives (ECAs). The function of the reagents and the formation mechanism of Ag hexagonal microsheets are also investigated. For the polyvinylpyrrolidone (PVP) and citrate facet-selective capping, the Ag atoms freshly reduced by N2H4 would orientationally grow alone on the {111} facet of Ag seeds, with the synergistically selective etching of irregular and small Ag particles by H2O2, to form Ag hexagonal microsheets. The hexagonal Ag microsheet-filled epoxy adhesives, as electrically conductive materials, can be easily printed on various substrates such as polyethylene terephthalate (PET), epoxy, glass, and flexible papers. The hexagonal Ag microsheet filled ECAs demonstrate lower bulk resistivity (approximately 8 × 10(-5) Ω cm) than that of the traditional Ag micrometer-sized-flake-filled ECAs with the same Ag content of 80 wt % (approximately 1.2 × 10(-4) Ω cm).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.