Abstract
The ternary catalyst Pt75Ru5Ni20 was conducted on various types of carbon supports including functionalized Vulcan XC-72R (f-CB), functionalized multi-walled carbon nanotubes (f-MWCNT), and mesoporous carbon (PC-Zn-succinic) by sodium borohydride chemical reduction method to improve the ethanol electrooxidation reaction (EOR) for direct ethanol fuel cell (DEFC). It was found that the particle size of the metals on f-MWCNT was 5.20 nm with good particle dispersion. The alloy formation of ternary catalyst was confirmed by XRD and more clearly described by SEM element mapping, which was relevant to the efficiency of the catalysts. Moreover, the mechanism of ethanol electrooxidation reaction based on the surface reaction was more understanding. The activity and stability for ethanol electrooxidation reaction (EOR) were investigated using cyclic voltammetry and chronoamperometry, respectively. The highest activity and stability for EOR were observed from Pt75Ru5Ni20/f-MWCNT due to a good metal-carbon interaction. Ru and Ni presented in Pt-Ru-Ni alloy improved the activity and stability of ternary catalysts for EOR. Moreover, the reduction of Pt content in ternary catalyst led to the catalyst cost deduction in DEFC.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.