Abstract
This paper reports a phase inversion method for the preparation of macroporous polysulfone (PS) composite spheres through a single orifice spinneret. Surfactant F127 was pre-added in the polymer solution as a surface pore-forming agent, and different amount of zeolitic imidazolate framework-8 (ZIF-8) particles were incorporated to form the ZIF-8/polysulfone (ZIF-8/PS)-composite spheres. ZIF-8 and polymer acted as the adsorbent and binder in the final composite spheres, respectively. The fabrication conditions, such as the types of the surfactant, the amount of the surfactant, and ZIF-8 added in the polymer solution, were investigated. Nitrogen and carbon dioxide sorption analysis indicated the ZIF-8/PS composite spheres had similar properties as the pure ZIF-8 particles, and the active sites of ZIF-8 in the polymer composites were well exposed. The composite spheres exhibited advantages of easy handling and recycling over ZIF-8 particles, and this phase inversion method can be extended to prepare other polymer composite spheres.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.