Abstract
AbstractThe light‐transmissive properties of a solid‐state tetrathiafulvalene radical cation‐bis(trifluoromethanesulfonyl)imide, 1‐C5⋅+ ⋅ NTf2−, underwent instantaneous changes in the short‐wave infrared (SWIR) region (1000–2500 nm) upon exposure to solvent vapor or the application of mechanostress at room temperature. The initial solid state of 1‐C5⋅+ ⋅ NTf2− exhibited strong absorption in the near‐infrared (NIR; 700–1000 nm) and SWIR regions, whereas the absorption in the SWIR region was significantly diminished in the stimulated state induced by dichloromethane vapor. Upon cessation of vapor stimulation, the solid state spontaneously and promptly reverted to its original state, characterized by absorption bands in the NIR/SWIR region. Moreover, the SWIR absorption was absent upon the application of mechanical stress using a steel spatula. The reversal was fast and occurred within 10 s. These changes were visualized using a SWIR imaging camera under 1450‐nm light irradiation. Experimental investigations demonstrated that the transparency to the SWIR light in the solid states was modulated through significant structural transformations of the associated radical cations, with transitions between columnar and isolated π‐dimer structures under ambient and stimulated conditions, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.