Abstract
Duplex stainless steel having attractive combination of austenitic and ferritic properties is being used in industry such as petrochemical, pulp and paper mills. In this study, the corrosion and stress corrosion behavior of duplex stainless steel in 3.5% sodium chloride environment was investigated by weight loss measurements, electrochemical DC testing and slow strain rate test (SSRT). Weight loss data showed no significant corrosion after 1700 hours. Electrochemical polarization test in 3.5% NaCl solution exhibited a uniform corrosion rate of 0.008 mpy (calculated using Tafel analysis) showing passivity in the range of 735-950 mV. A comparison of the slow strain rate test in 3.5% NaCl solution with air shows almost a similar stress strain curve for duplex stainless steel. In comparison, the stress strain curves for 0.15% carbon steel show a loss of about 25% tensile elongation for the same comparison. The excellent corrosion and especially resistance to localized corrosion (pitting) is responsible for no loss of ductility in duplex stainless steel.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.