Abstract
Optical absorption and photoluminescence (PL) measurements were performed on single crystals of undoped Y3Al5O12 (YAG) and a number of rare-earth-doped YAG to study the effect of dopant type and concentration, growth atmosphere, post-growth annealing and UV irradiation on the optical properties of YAG crystals. The presence of hydrogen in the growth atmosphere was found to be essential for enhancing the incorporation of Ce ions in the Ce3+ state in Ce-doped YAG (Ce : YAG). Annealing in air was shown to have no effect on the PL emission of Ce : YAG crystals. An absorption peak around 256 nm was observed in the undoped YAG and Ce : YAG crystals after air anneal at 1200 °C. Optical absorption and annealing experiments support the association of the 256 nm peak with Fe impurities and oxygen ions. UV irradiation modifies the valency of impurities and generates electronic defects leading to an increase in the optical density of YAG crystals. Optimizing the growth and annealing conditions is critical in order to develop Ce : YAG single crystals as efficient scintillators.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.