Abstract
Thermal cycling has been observed to cause a transition from superficial alumina formation to internal oxidation and nitridation, an effect that was shown to depend on the specimen thickness and geometry, which can be described by a spalling-probability model. Once protection by a dense and adherent alumina scale got lost, the internal-corrosion rate is determined by the diffusivity and solubility of nitrogen and oxygen in the alloy. These parameters seem to depend not only on the temperature and the alloy composition but also on the applied mechanical stress. Internal nitridation under a superimposed creep loading was found to follow a higher rate constant than under just isothermal exposure. This effect can probably be attributed to dislocation-pipe diffusion, a mechanism which has been claimed also to be relevant for outward solvent diffusion during internal corrosion, a phenomenon, which was observed as a stress-relief mechanism during various internal-reaction processes
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.