Abstract
Recent studies on the room-temperature fracture behavior of Ni3Al-Zr alloys after preexposure at elevated temperatures show various types of intergranular failure. In the presently studied Ni78Al21Zr1B0.2 alloy, a strong intergranular fracture tendency at room temperature has been found after preexposure at 750 °C, which is caused by the grain boundary precipitation in this alloy. After short-term exposure above 1200 °C and bending fracture at room temperature, the alloy also suffers intergranular embrittlement due to grain boundary melting. The intergranular fracture appearance is quite different from that observed in a previous study for a Ni77.4Al22Zr0.6B0.2 alloy after air exposure for 100 hours at 1200 °C. In that case, the intergranular fracture was accompanied by grain boundary diffusion (invasion) and segregation of oxygen. The mechanisms of these types of grain boundary failure are discussed.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call