Abstract
Thicker bondlines along with manufacturing-tolerant and fracture-resistant adhesives are trends visible across different industries, especially maritime. In this work, two contrasting adhesives: an elastic-brittle epoxy-based, and a nonlinear-ductile methyl methacrylate (MMA) are characterized and compared via tensile, compact tension (CT) and double cantilever beam (DCB) testing, for steel-to-steel adherends. Significant differences are captured between the two bonding materials in terms of the energy required for crack growth: in the MMA “ductile” adhesive is ∼4 and 10 times more than for the epoxy “relatively brittle” adhesive for CT and DCB testing, respectively. While epoxy bondlines fail due to a symmetric in-plane crack, the MMA bondlines experience multiple cracking originating from high deformations and Poisson's effects. Moreover, in the case of MMA adhesive, the DCB testing led to plastic deformation of steel adherends. The existing evaluation protocols are adopted for data reduction and the effect of plastic dissipation is theoretically addressed. Despite adherend plasticity, it is concluded that the crack growth is driven by the elastic energy release, and thus, after small correction taking into account initial adherend plasticity, the existing simple models can still be used. This study highlights the potential use of ductile adhesive instead of the commonly used brittle ones to significantly improve the adhesively bonded joints in maritime applications in which thick bondlines, manufacturing-tolerant and fracture-resistance characteristics are required.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.