On the evolution of dislocation cell structures in two Al-alloys (Al-5Mg and Al-11Zn) during reciprocal sliding wear at high homologous temperatures

Abstract

The formation of dislocation substructures in up to 10 µm deep subsurface regions of two aluminium alloys, Al-5Mg and Al-11Zn, was investigated under conditions of high homologous temperature reciprocal sliding wear (HT-RSW). Under creep conditions, Al-5Mg shows a solid solution type of inverse primary creep. In contrast, Al-11Zn creeps obstacle controlled and exhibits normal primary creep. These two materials were subjected to reciprocal sliding wear at 200 and 300 °C for 100 and 1000 cycles. Flat polished disks were exposed to the 1 mm reciprocal movements of a spherical aluminium oxide counterbody under normal forces of 5 and 10 N at an oscillation frequency of 1 Hz. Using focused ion beam (FIB) micromachining thin electron transparent foils were prepared from the surface regions of the as received and worn material states. Transmission electron microscopy (TEM) was used to study the evolution of nano and micro grain sizes in the surface regions. Despite the different creep behavior, the two materials behave similar under conditions of reciprocal sliding wear. The results obtained in the present work show that subgrain sizes decrease with increasing numbers of wear cycles and increasing normal forces. Subgrain sizes also increase with increasing temperature. At 300 °C, dynamic recrystallization was observed in both Al-alloys. The results of the present work are discussed in the light of previous results reported in the literature. Areas in need of further work are highlighted.