Abstract
A polymer space-holder method was used in this study to prepare porous coppers with low-to-medium porosity within the range 5–50%. This provides the possibility to control the pore size, distribution and structure. Optical microscopy and scanning electron microscopy (SEM) with energy dispersion spectrum (EDS) were utilized to characterize the porous samples. Two different sizes of copper powders, 5 and 45 μm, were used to investigate the effect of raw materials powder size. Microstructure results have shown that there exist two different types of pore in the sintered samples: round-shaped macro-pores left over by the burnout of the space holder and irregular micro-pores or the intervals among metal powders. No matter which size powder was used, the size of the macro-pore falls into a range 200–500 μm, but the pore structures are different in the two cases, interconnected or open pores for the 45 μm raw powders and closed pore for the 5 μm powders. The sizes of the micro-pores among the copper powders in the two cases are also different, several microns for the 5 μm powders and 10–20 μm for the 45 μm powders, though all micro-pores are interconnected for both powder sizes. From the viewpoint of pore structure, it is concluded that the 45 μm powder is more appropriate for use to prepare the porous metal. In addition, the effect of the binder was also investigated. It is suggested that a binder that can be easily and completely removed should be used in order to induce the residue. This paper, as Part II of the publication, focuses on the fabrication of the porous samples where Part I [Lemons JE, editor. Quantitative characterization and performance of porous implants for hard tissue application. ASTM STP 953; 1985] has been published earlier for the mechanical properties of the material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.