Abstract
Antiferromagnetic/ferromagnetic (AF/F) NiMn/Fe37Co48Hf15 films were investigated with respect to their exchange bias, in-plane unidirectional anisotropy, polarisation and high frequency behaviour. After deposition, carried out by r.f. magnetron sputtering, the films were post-annealed for 4h at 300°C in a static magnetic field, in order to induce exchange-bias, which results in a unidirectional anisotropy. Dependent on the presence of a bi-layer or multi-layer sandwich structure the films show a different exchange-bias field–ferromagnetic inter-layer thickness behaviour with exchange-bias fields μ0⁎Heb between 2 and 10mT. The in-plane uniaxial (single film) or unidirectional anisotropy fields μ0*HUF were between 4 and 18mT. This results in a significant increase of the cut-off frequency in the GHz range in comparison to a single Fe37Co48Hf15 film, which is shown by frequency-dependent permeability plots. High damping in the imaginary part of the permeability, i.e., high resonance line broadening could be observed for films with high coercivity μ0*Hc of around 7mT in the easy axis of magnetisation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.